Product Details:
|
| Raw Material: | 100% Virgin PP | Appearance: | Fibrillated Mesh |
|---|---|---|---|
| Crack Elongation (%): | >10 | Melting Point (℃): | 160 |
| Density: | 0.91 | Tensile Strength (Mpa): | >560 |
| Fiber Diameter (mm): | 0.035 | Elastic Modulas (Mpa): | >3500 |
| Width (mm): | 5 | Alkali & Acid Resistance: | Strong |
| Application: | Improve Concrete Reinforcement ,mortar Reinforcement,anti-cracking Resistance | Packing: | 0.9 Or 1kg |
| Concrete Ratio Design: | Fiber Content Is 0.9kg/m3 | Bridge Waterlayer Ratio Design: | Fiber Content Is 1.35-1.8kg/m3 |
| The Commonly Used Concrete Fiber Length: | 20mm | ||
| Highlight: | 100% Virgin Polypropylene PP Fiber,Concrete PP Fiber Mesh,Mesh Form Polypropylene PP Fiber |
||
100% virgin polypropylene PP Fiber Mesh Form For Concrete Reinforcement
PP Fiber Mesh Function:
1.PP fiber mesh can improve plastic deformity
2.PP fiber mesh can prolong endurance
3.PP fiber mesh can improve steel protection
4.PP fiber mesh can improve fire resistance Strengthen spurt & fatigue
5.PP fiber mesh can improve tensile, bending & folding strength
6.PP fiber mesh have Strong acid & alkali resistance and good endurance
7.PP fiber mesh can increase seepage resistance and cracking resistance
PP Fiber Mesh Specifications:
| Raw Material | 100% virgin polypropylene | Fiber type | Fibrillated Mesh |
| Crack Elongation (%) | 10 min. | Melting Point (℃) | 160 |
| Density | 0.91 | Tensile Strength (Mpa) | 560 min. |
| Fiber Diameter (mm) | 0.035 | Fiber length (mm) | 12,19,38,54... |
| Elastic Modulas (Mpa) | 3500 min. | Width (mm) | 5 |
| Alkali & Acid resistance | Strong | Water-Absorbency | No. |
PP Fiber Mesh Application:
1.It can be used for concrete reinforcement
2.It can be used for mortar reinforcement
3.It can be used for anti-cracking resistance
PP Fiber Mesh Instruction:
1. PP fiber mesh Length : The commonly used fiber length in concrete is 20mm, and the commonly used fiber length in shotcrete is 10mm
2. PP fiber mesh ratio Design: Usually the fiber content of concrete is 0.9kg/m3, the fiber content of bridge waterproof layer is required to be 1.35-1.8kg/m3, the tunnel spray concrete is the same, and other materials remain unchanged. Among a series of active composite materials such as silica fume, pulverized coal, grinding slag, zeolite powder and fiber, fiber has a relatively good effect on concrete.
3. PP fiber mesh mixer Adoption:Double-axis horizontal compelling mixer and self-dropping cylinder mixer, Double-axis horizontal compelling mixer is better,self-dropping cylinder mixer is used,too.
4.PP fiber mesh mixing process: The crushed stone, fiber, sand into the blender. Stir normally for two minutes, until the fiber is fully developed, then add cement and water, and stir. Usually the material can be put in as usual, but the mixing time should be extended to ensure that the fiber can be fully and evenly mixed.
5.PP fiber mesh stirring time: The purpose of mixing is to make the fiber fully spread into monofilament or net fully spread, so after adding the polypropylene fiber net, the concrete mixture is usually stirred for 2-3 minutes.
PP Mesh Fiber Packing:
0.9kg or 1kg net each PE bag or paper bag