Raw:100%
Fiber:Fibrillated Mesh
Crack:10%min
Density(g/cm3):0.91
Tensile Strength (Mpa):500 min.
Melting Point(℃):160—170
acid&alkali resistance:Excellent
Break tensile ratio:15% min.
Break Strength:600Mpa
Acid &Alkali Resistance:Strong
Crack Elongation:15-20%
Elastic Modulas (MPa) -:5192
Minimum Tensile Strength:≥550Mpa
Modulus:≥9000Mpa
Fiber Dimension:L: 48mm/54mm/64mm;T: 0.55-0.60mm; W: 1.30- 1.40mm
Raw Material:Polypropylene
Fiber Type:wave form
Length:24-60mm
Raw Material:Polypropylene
Fiber Type:wave form
Melting Point(℃):160— 170
Minimum Tensile Strength:Minimum Tensile Strength
Modulus:≥9000Mpa
Fiber Dimension:L: 48mm/54mm/64mm;T: 0.55-0.60mm; W: 1.30- 1.40mm
Raw Material:PP/PE
Elastic Modulus:≥5000Mpa
Break Strength:600Mpa
Modulus:≥9000Mpa
Fiber Dimension:L: 48mm/54mm/64mm;T: 0.55-0.60mm; W: 1.30- 1.40mm
Melt Point:170℃
Raw Material:100% virgin Polypropylene
Density(g/cm3):0.91
Tensile Strength (Mpa):500 min.
Density:0.91
Raw material:100％ virgin PP
Width:5mm